Hard UV Resin
$38.50 – $67.50
Rigid prototyping resin with crisp details, high stiffness and hardness. Parts printed with this resin won’t deform when pressure is applied.
1Kg
Key Features:
• Rigid
• Quick curing
• High stiffness
Applications:
• Protoyping
• Engineering
Compatible Printers:
UV LCD Printers such as LC Dental, MoonRay, Asiga, Envisontec, Flashforge, Anycubic, Wanhao, Phrozen, Sparkmaker, Kudo Bean and more.
Properties
Hard UV Resin
Tensile Properties
Tensile Modulus *
Tensile Strength *
Elongation at break *
2060 MPa
35 MPa
4%
ASTM D638
ASTM D638
ASTM D638
General Properties
Hardness *
Heat Deflection Temperature *
Viscosity
Density
Storage
Colour
77 Shore D
60 °C
230 cPs
1.19 g/cm3
10<T>50°C
Black, Grey
ASTM D2240
ASTM D648 (0.455 MPa)
At 25°C Brookfield spindle 3
* Post cured for 1hr at 60°C in Cure M+
Key Features:
• Rigid
• Quick curing
• High stiffness
Applications:
• Protoyping
• Engineering
Compatible Printers:
UV LCD Printers such as LC Dental, MoonRay, Asiga, Envisontec, Flashforge, Anycubic, Wanhao, Phrozen, Sparkmaker, Kudo Bean and more.
Properties
Hard UV Resin
Tensile Properties
Tensile Modulus *
2060 MPa
ASTM D638
Tensile Strength *
35 MPa
ASTM D638
Elongation at break *
4%
ASTM D638
General Properties
Hardness *
77 Shore D
ASTM D2240
Heat Deflection Temperature *
60 °C
ASTM D648 (0.455 MPa)
Viscosity
230 cPs
At 25°C Brookfield spindle 3
Density
1.19 g/cm3
Storage
10<T>50°C
Colour
Black, Grey
* Post cured for 1hr at 60°C in Cure M+
Glossary of Key Terms
Tensile strength: Ability for an object to withstand pulling (tensile) force. Measured in units of force per cross-sectional area.
% elongation: How much an object can be stretched from its original shape.
Young’s Modulus: How much force is needed to stretch an object.
Flexural Strength: Ability to resist deformation under load.
Flexural Modulus: Measurement of an objects resistance to bend when force is applied (bend modulus).
HDT: Temperature at which a plastic deforms under heat.