Rigid DL240 Plant-Based 3D Resin
$405.00
Rigid DL240 Plant-Based 3D resin is a high-performance rigid 3D printing resin which consists of 50% plant based raw materials, offering a substantial reduction on net CO2 emission compared to conventional resins.
Best Used for:
• Fast and accurate prototyping
• Dental models for aligner manufacturing
USPs:
• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally.
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production.
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles
Compatible Printers:
LC Magna (Not suitable for UV 3D printers)
Properties
Rigid DL240 Plant-Based Resin
Tensile Properties
Green
Post-cured*
Method
Tensile Modulus
Tensile Strength (Break)
Tensile Strength (Yield)
Elongation at break
1210 MPa
27 MPa
24.3 MPa
19.2%
2440 MPa
56.6 MPa
64.5 MPa
6.1%
ASTM D638
ASTM D638
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength
Flexural Modulus
–
–
108 MPa
2656 MPa
ASTM D790
ASTM D790
Impact Properties
Impact Strength Notched Izod
Impact Strength Notched Izod
–
–
12.2 J/m
2.2 J/m
ASTM D256
ISO 180
General Properties
Shore Hardness
HDT (@ 0.455 MPa)
HDT (@ 1.82 MPa)
Water Absorption %* after 24 hrs
Water Absorption %* after 72 hrs
Water Absorption %* after 7 days
–
–
–
88 Shore D
78.4 °C
62.6 °C
0.470%
0.625%
0.933%
ASTM D2240
ASTM D648
ASTM D648
ASTM D570
ASTM D570
ASTM D570
Liquid Properties
Viscosity
Density
Storage
Color
–
–
–
580 cPs
1.10 g/cm3
10<T>50°C
Translucent
At 25°C Brookfield spindle 3
* Post cured for 2 hours at 60°C with Photocentric Cure L2
Best Used for:
• Fast and accurate prototyping
• Dental models for aligner manufacturing
USPs:
• High accuracy
– Over 98% of scanned data within +/- 100μm for dental models printed horizontally.
– Over 83% of scanned data within +/- 100μm for dental models printed vertically, increasing output for overnight production.
• Exceptional surface finish and smooth feel
• Fast post-curing
• Dry to touch
• Rigid
• 50% of components from plant-based materials
• Enabling quick design iterations by offering 250 and 350μm layer thickness print profiles
Compatible Printers:
LC Magna (Not suitable for UV 3D printers)
Properties
Rigid DL240 Plant-Based Resin
Tensile Properties
Tensile Modulus
1210 MPa | 2440 MPa*
ASTM D638
Tensile Strength (Break)
27 MPa | 56.6 MPa*
ASTM D638
Tensile Strength (Yield)
24.3 MPa | 64.5 MPa*
ASTM D638
Elongation at break
19.2% | 6.1%*
ASTM D638
Flexural Properties
Flexural Strength
108 MPa*
ASTM D790
Flexural Modulus
2656 MPa*
ASTM D790
Impact Properties
Impact Strength Notched Izod
12.2 J/m
ASTM D256
2.2 kJ/m2
ISO 180
General Properties
Shore Hardness
84 Shore D*
ASTM D2240
HDT (@ 0.455 MPa)
78.4°C*
ASTM D648
HDT (@ 1.82 MPa)
62.6°C*
ASTM D648
Water absorption (%)* after 24 hrs
0.470%
ASTM D570
Water absorption (%)* after 72 hrs
0.625%
ASTM D570
Water absorption (%)* after 7 days
0.933%
ASTM D570
Liquid Properties
Viscosity
580 cPs
At 25°C Brookfield spindle 3
Density
1.10 g/cm3
Storage
10<T>50°C
Color
Translucent
* Post cured for 2 hours at 60°C with Photocentric Cure L2