Durable UV80

$105.00$420.00

Photocentric Durable range is the most versatile material of the Photocentric functional materials, resisting impact, compression, bending, and stress fatigue without breaking or deforming.
Photocentric Durable UV80 works with a variety of UV LCD and DLP 3D printers, as well as the Photocentric Liquid Crystal Dental printer.

Best Used for:

• Jigs and fixtures requiring minimal deflection
• Cover-plates and enclosures
• Fastenings, tools and couplings
• Suitable for end-use parts

USPs:

• Tough, durable, and long lasting
• Simulating the strength and stiffness of ABS
• High definition
• Smooth surface finish

Compatible Printers:

UV 3D Printers, LC Dental

Clear
SKU: N/A Categories: , , , , Tag:

Properties

Tensile Properties

Tensile Modulus *

Ultimate Tensile Strength *

Elongation at break *

1940 MPa

46 MPa

13%

ASTM D638

ASTM D638

ASTM D638

Flexural Properties

Flexural Strength *

Flexural Modulus *

28 MPa

760 MPa

ASTM D790

ASTM D790

Impact Properties

Impact Strength Notched Izod *

8.1 kJ/m2

ISO 180

General Properties

Hardness *

Heat Deflection Temperature *

Viscosity

Density

Storage

Color

84 Shore D

65 °C

400 cPs

1.10 g/cm3

10<T>50°C

Black

ASTM D2240

ASTM D648

At 25°C Brookfield spindle 3

* Post cured for 2hrs at 60°C in CureM+

Download TDS >          Download SDS >         

 

Properties

Tensile Properties

Tensile Modulus *

1940 MPa

ASTM D638

Ultimate Tensile Strength *

46 MPa

ASTM D638

Elongation at break *

13%

ASTM D638

Flexural Properties

Flexural Strength *

28 MPa

ASTM D790

Flexural Modulus *

760 MPa

ASTM D790

Impact Properties

Impact Strength Notched Izod *

8.1 kJ/m2

ISO 180

General Properties

Hardness *

84 Shore D

ASTM D2240

Heat Deflection Temperature *

65 °C

ASTM D648

Viscosity

400 cPs

At 25°C Brookfield spindle 3

Density

1.10 g/cm3

Storage

10<T>50°C

Color

Black

 

* Post cured for 1hr at 60°C in Cure L2