Daylight Magna High Tensile Resin

$420.00

When strong parts are required, Magna High Tensile is the resin of choice. Capable of producing incredibly detailed parts along with great strength, higher than that of injection moulded Polycarbonate with similar mechanical behaviour. Our 3D High Tensile Resin enables you to 3D print extremely strong and durable parts while maintaining an incredibly high accuracy.

1 in stock

5Kg

SKU: MAGHTWH05 Categories: , , , Tag:

Best used for:

• Engineering
• Prototyping
• Tooling and moulds

Compatible Printers:

LC Magna (Not suitable for UV 3D printers)

Unique features:

• High tensile modulus
• High accuracy
• Smooth surface finish
• Minimal shrinkage
• Heat deflection temperature of 95°C

Properties

Tensile Properties

Tensile Modulus *

Ultimate Tensile Strength *

Elongation at break *

3060 MPa

81 MPa

4.8%

ASTM D638

ASTM D638

ASTM D638

Flexural Properties

Flexural Strength *

Flexural Modulus *

95 MPa

2200 MPa

ASTM D790

ASTM D790

Impact Properties

Impact Strength Notched Izod *

22.7 J/m

ASTM D256

General Properties

Hardness *

Heat Deflection Temperature *

Viscosity

Density

Storage

92 Shore D

203 °F

980 cPs

1.16 g/cm3

10<T>50°C

ASTM D2240

ASTM D648 (0.455 MPa)

At 25°C Brookfield spindle 3

*Mechanical properties stated based on fully cured material.

Best used for:

• Engineering
• Prototyping
• Tooling and moulds

Compatible Printers:

LC Magna (Not suitable for UV 3D printers)

Unique features:

• High tensile modulus
• High accuracy
• Smooth surface finish
• Minimal shrinkage
• Heat deflection temperature of 95°C

Properties

Tensile Properties

Tensile Modulus *

3060 MPa

ASTM D638

Ultimate Tensile Strength *

81 MPa

ASTM D638

Elongation at break *

4.8%

ASTM D638

Flexural Properties

Flexural Strength *

95 MPa

ASTM D790

Flexural Modulus *

2200 MPa

ASTM D790

Impact Properties

Impact Strength Notched Izod *

22.7 J/m

ISO 180

General Properties

Hardness *

92 Shore D

ASTM D2240

Heat Deflection Temperature *

203 °F

ASTM D648 (0.455 MPa)

Viscosity

980 cPs

At 25°C Brookfield spindle 3

Density

1.16 g/cm3

 

Storage

10<T>50°C

*Mechanical properties stated based on fully cured material.

Glossary of Key Terms
Tensile strength: Ability for an object to withstand pulling (tensile) force. Measured in units of force per cross-sectional area.

% elongation: How much an object can be stretched from its original shape.

Young’s Modulus: How much force is needed to stretch an object.

Flexural Strength: Ability to resist deformation under load.

Flexural Modulus: Measurement of an objects resistance to bend when force is applied (bend modulus).

HDT: Temperature at which a plastic deforms under heat.

Reviews

    Be the first to review “Daylight Magna High Tensile Resin”

    Your email address will not be published.