Flexible DL220B Resin
$462.00
Daylight Flexible Resin- ‘Flexible DL220B’ is an optimised solution for applications which require a combination of impact absorption, high elongation, efficient energy damping, good tear strength and exceptionally low water absorption.
5Kg
Best Used for:
• Sport protection, e.g., shin pads
• Shock and impact absorption, e.g., phone cases
• Cushioning
• Vibration damping, e.g., industrial machinery feet
USPs:
• Remarkable elongation at break >200%
• Slow rebound and efficient energy damping
• Exceptionally low water absorption (<1% after 7 days)
• High definition and resolution
• Easy to print due to its high green strength
Compatible Printers:
LC Magna (Not suitable for UV 3D printers)
Properties
Flexible DL220B Resin
Tensile Properties
Green
Post-cured*
Method
Tensile Modulus
Tensile Strength (Break)
Elongation at break
20 MPa
27 MPa
107%
66.4 MPa
14 MPa
211%
ASTM D412
ASTM D412
ASTM D412
Mechanical Properties
Tear Strength
Rebound Resilience
–
–
21 kN/m
19.6%
ASTM 624 Type C
ASTM D7121
General Properties
Shore Hardness
Water Absorption %* after 24 hrs
Water Absorption %* after 72 hrs
Water Absorption %* after 7 days
–
–
–
–
80 Shore A
0.32%
0.53%
1.09%
ASTM D2240
ASTM D570
ASTM D570
ASTM D570
Liquid Properties
Viscosity
Density
Storage
Color
–
–
–
1600 cPs
1.06 g/cm3
10<T>50°C
Black Translucent
At 25°C Brookfield spindle 3
* Post cured for 10 hours at 60°C with Photocentric Cure L2
Best Used for:
• Sport protection, e.g., shin pads
• Shock and impact absorption, e.g., phone cases
• Cushioning
• Vibration damping, e.g., industrial machinery feet
USPs:
• Remarkable elongation at break >200%
• Slow rebound and efficient energy damping
• Exceptionally low water absorption (<1% after 7 days)
• High definition and resolution
• Easy to print due to its high green strength
Compatible Printers:
LC Magna (Not suitable for UV 3D printers)
Properties
Flexible DL220B Resin
Tensile Properties
Tensile Modulus
20 MPa | 66.4 MPa*
ASTM D412
Tensile Strength (Break)
2.6 MPa | 14 MPa*
ASTM D412
Elongation at break
107% | 211%*
ASTM D412
Mechanical Properties
Tear Strength
21 kN/m
ASTM 624 Type C
Rebound Resilience
19.6%
ASTM D7121
General Properties
Shore Hardness
80 Shore A*
ASTM D2240
Water absorption (%)* after 24 hrs
0.32%
ASTM D570
Water absorption (%)* after 72 hrs
0.53%
ASTM D570
Water absorption (%)* after 7 days
1.09%
ASTM D570
Liquid Properties
Viscosity
1600 cPs
At 25°C Brookfield spindle 3
Density
1.06 g/cm3
Storage
10<T>50°C
Colour
Black Translucent
* Post cured for 10 hours at 60°C with Photocentric Cure L2