Daylight Magna Draft Resin

$420.00

Our Daylight Magna Draft 3D printing resin  is our fastest printing resin yet. Specifically designed to allow for detailed, large parts to printed in shorter times for rapid prototyping or even production. This resin works up to a 350 μm layer height with low curing times, reducing print times dramatically. The end parts manufactured exhibit very high strength comparable to acrylic and polyimide.

In stock

5Kg
SKU: MAGDRBU05 Categories: , , Tag:
Best used for:

• Ideal for prototyping
• Fast printing
• Translucency allows for easy inspection of hollowed parts

Compatible Printers:

LC Magna (Not suitable for UV 3D Printers)

Unique features:

• Printed parts exhibit very high strength
• Resilient with little compression
• Fast post curing

Properties
Tensile Properties
Tensile Modulus *
Ultimate Tensile Strength *
Elongation at break *
3200 MPa
84 MPa
4.4%
ASTM D638
ASTM D638
ASTM D638
Flexural Properties
Flexural Strength *
Flexural Modulus *
109 MPa
2840 MPa
ASTM D790
ASTM D790
Impact Properties
Impact Strength Notched Izod *
22.6 J/m
ASTM D256
General Properties
Hardness *
Heat Deflection Temperature*
Viscosity
Density
Storage
Colour
90 Shore D
167°F
970 cPs
1.16 g/cm3
10<T>50°C
Turquoise
ASTM D2240
ASTM D648
At 25°C Brookfield spindle 3
Biocompatibility
Cytotoxicity*
Passed
ISO 10993-5
*Mechanical properties stated based on fully cured material.
Best used for:

• Ideal for prototyping
• Fast printing
• Translucency allows for easy inspection of hollowed parts

Compatible Printers:

LC Magna (Not suitable for UV 3D Printers)

Unique features:

• Printed parts exhibit very high strength
• Resilient with little compression
• Fast post curing

Properties
Tensile Properties
Tensile Modulus *
3200 MPa
ASTM D638

 

Ultimate Tensile Strength *
84 MPa
ASTM D638

 

Elongation at break *
4.4%
ASTM D638
Flexural Properties
Flexural Strength *
109 MPa
ASTM D790

 

Flexural Modulus *
2840 MPa
ASTM D790
Impact Properties
Impact Strength Notched Izod *
22.6 J/m
ASTM D256
General Properties
Hardness *
90 Shore D
ASTM D2240

 

Heat Deflection Temperature*
167°F
ASTM D2240

 

Viscosity
970 cPs
At 25°C Brookfield spindle 3

 

Density
1.16 g/cm3

 

Storage
10<T>50°C

 

Colour
Turquoise
Biocompatibility
Cytotoxicity*
Passed
ISO 10993-5

 

*Mechanical properties stated based on fully cured material.

 